GENERAL:
AN AUSTENITIC CHROMIUM NICKEL STAINLESS STEEL WITH ADDED TITANIUM.
USES:
SUITABLE FOR MANUFACTURE OF PARTS INTRMITTENTLY HEATED TO TEMPERATURES
BETWEEN 427/899 CENTIGRADE.
CHEMICAL
ANALYSIS: |
C |
SI |
MN |
S |
P |
0.08MAX |
1.00MAX |
2.00MAX |
0.03MAX |
0.045MAX |
|
Cr |
Ni |
Ti |
|
|
17.00/19.00 |
9.0/12.0 |
5C/0.80 |
|
|
|
TYPICAL
MECHANICAL PROPERTIES: (EXAMPLE ONLY) |
TEN. STRENTH |
YIELD STRESS |
ELONG |
510Nmm |
2 235Mmm2 |
35%MIN |
HEAT TREATMENT & CONDITION
HAS HIGHER TENSILE AND CREEP STRENGHT AT
ELEVATED TEMPERATURES THAN CONVETIONAL 18/8 ALLOYS.
DESIGNED TO ELIMINATE INTERGRANULAR CORROSION IN THE AS
WELDED CONDITION.
SECTIONS
COMMERCIALY AVAILABLE IN ROUNDS, FLATS, AND
HEXAGONS